Cathode active material and lithium secondary battery containing them

ABSTRACT

Provided is a non-aqueous electrolyte-based, high-power lithium secondary battery having a long service life and superior safety at both room temperature and high temperature, even after repeated high-current charging and discharging. The battery comprises a mixture of a lithium/manganese spinel oxide having a substitution of a manganese (Mn) site with a certain metal ion and a lithium/nickel/cobalt/manganese composite oxide, as a cathode active material.

FIELD OF THE INVENTION

The present invention relates to a non-aqueous electrolyte-based,high-power lithium secondary battery having a long-term service life andsuperior safety at both room temperature and high temperature, evenafter repeated high-current charge and discharge.

BACKGROUND OF THE INVENTION

Technological development and increased demand for mobile equipment haveled to a rapid increase in the demand for secondary batteries as anenergy source. In recent years, applicability of secondary batteries hasbeen realized as power sources for electric vehicles (EVs) and hybridelectric vehicles (HEVs). In the light of such trends, a great deal ofresearch and study has been focused on secondary batteries which arecapable of meeting various demands. Among other things, there has beenan increased demand for lithium secondary batteries having high-energydensity, high-discharge voltage and power output stability.

Particularly, lithium secondary batteries for use in EVs require notonly high-energy density and capability to exert large power outputwithin a short period of time, but also a long-term service life of morethan 10 years even under severe conditions in which high-currentcharge/discharge cycles are repeated within a short time, thusnecessitating remarkably superior safety and long-term service lifecompared to conventional small-size lithium secondary batteries.

Lithium ion secondary batteries that have been used in conventionalsmall-size batteries generally employ a layered structure of lithiumcobalt composite oxide as a cathode material and a graphite-basedmaterial as an anode material. However, the main constitutional elementof the lithium cobalt composite oxide, cobalt, is very expensive and isnot suitable for use in electric vehicles due to safety concerns.Therefore, as the cathode material of lithium ion batteries for EVs, alithium manganese composite oxide having a spinel structure made up ofmanganese is ideal in terms of both cost and safety.

However, the lithium manganese composite oxide, upon high-temperatureand high-current charge/discharge, undergoes elution of manganese ionsinto an electrolyte due to the influence of the electrolyte, thusresulting in degradation of battery properties and performance. Thus,there is a need for measures to prevent such problems. In addition, thelithium manganese composite oxide has drawbacks such as a low capacityper unit weight, i.e., a low charge density, as compared to conventionallithium cobalt composite oxides or lithium nickel composite oxides.Thus, there is a limit to charge density of the battery and in order toenter practical use as the power source of EVs, HEVs and the like,designs of the battery to solve such disadvantages should be effectedtogether.

In order to alleviate the above-mentioned respective disadvantages,various studies and attempts to fabricate electrodes using a mixedcathode active material have been made. For example, Japanese PatentLaid-open Publication Nos. 2002-110253 and 2004-134245 disclosetechniques utilizing a mixture of lithium/manganese composite oxide, andlithium/nickel/cobalt/manganese composite oxide and/orlithium/nickel/cobalt/manganese composite oxide to enhance recoveryoutput and the like. These arts, however, still suffer from problemsassociated with a poor cycle life of the lithium manganese oxide andlimited improvement of safety.

SUMMARY OF THE INVENTION

Therefore, it is an object of the present invention to solve the aboveproblems, and other technical problems that have yet to be resolved.

Specifically, an object of the present invention is to provide a cathodeactive material for a secondary battery, comprising a mixture of amanganese spinel oxide having a substitution of a manganese (Mn) sitewith a certain metal element and a lithium/nickel/cobalt/manganesecomposite oxide, whereby the battery can secure safety and, due toalleviation of disadvantages of the lithium/manganese oxide, can have along-term service life at both room temperature and high temperature,even after repeated high-current charge and discharge.

Another object of the present invention is to provide a lithiumsecondary battery comprising the above-mentioned cathode activematerial, upon fabrication of the cathode.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

In accordance with an aspect of the present invention, the above andother objects can be accomplished by the provision of a cathode activematerial for a lithium secondary battery, comprising a mixture of alithium/manganese spinel oxide represented by Formula I below and alithium/nickel/cobalt/manganese composite oxide represented by FormulaII below:Li_(1+x)Mn_(2−y)M_(y)O₄  [Formula I]wherein,

M is a metal having an oxidation number of 2 to 3;

0≦x≦0.2; and

0<y≦0.2.Li_(1+z)Ni_(b)Mn_(c)Co_(1−(b+c))O₂  [Formula II]wherein,

0≦z≦0.1;

0.2≦b≦0.7;

0.2≦c≦0.7; and

b+c<1.

In accordance with another aspect of the present invention, there isprovided a lithium secondary battery comprising the above-mentionedcathode active material-containing cathode, an anode, a separator and anon-aqueous electrolyte.

Hereinafter, the present invention will be described in more detail.

As discussed hereinbefore, the present invention is characterized byusing a mixture of the lithium/nickel/cobalt/manganese oxide and thelithium/manganese spinel oxide wherein a portion of manganese (Mn) issubstituted with other metal elements, as a cathode active material.

In the lithium/manganese spinel oxide of Formula I, manganese (Mn) issubstituted with a metal (M) having an oxidation number of 2 or 3 withinthe predetermined range. Herein, the metal (M) may be preferablyaluminum (Al), magnesium (Mg) or both of them.

Since the oxidation number of the substituent metal is smaller than thatof manganese (Mn), an increasing amount of the substituted metal leadsto a decrease in an average value of the oxidation number and a relativeincrease in the oxidation number of manganese (Mn), consequentlyresulting in inhibition of manganese (Mn) dissolution. That is, lifecharacteristics are further improved as the amount of the substitutedmetal (y) in the lithium/manganese spinel oxide increases. However,since an increasing amount of the substituted metal (y) is alsoaccompanied by a decrease of initial capacity, a maximum value of y ispreferably less than 0.2, which is capable of maximizing improvements ofthe life characteristics and minimizing reduction of the initialcapacity of the battery. More preferably, the value of y is in the rangeof 0.01 to 0.2.

Where appropriate, high-temperature cycle characteristics and capacitypreservation characteristics may be improved to some extent by adjustingthe composition ratio of constituent elements in the lithium/manganesespinel oxide, but there are limitations to high-temperature safety andcapacity per weight.

Therefore, as the cathode active material, the present invention usesthe lithium/manganese spinel oxide in admixture with a certainlithium/nickel/cobalt/manganese composite oxide of Formula II which isan active material expected to increase a service life due to a higherstability thereof

The lithium/nickel/cobalt/manganese composite oxide is a lithium oxidewhich simultaneously contains nickel, manganese and cobalt elements, asshown in Formula II, and significantly improves, in combination with thelithium/manganese spinel oxide, the safety and life characteristics ofthe cathode active material according to the present invention. Thelithium/nickel/cobalt/manganese composite oxide contains each of atleast 0.2 M nickel and manganese, provided that it contains cobalt.Preferred examples of the lithium/nickel/cobalt/manganese compositeoxide may include, but are not limited to,Li_(1+z)Ni_(1/3)Co_(1/3)Mn_(1/3)O₂ andLi_(1+z)Ni_(0.4)Mn_(0.4)Co_(0.2)O₂. Particularly, thelithium/nickel/cobalt/manganese composite oxide having a relatively highcontent of nickel compared to that of manganese and cobalt is morepreferred for realization of high capacity.

The mixing ratio of the lithium/manganese spinel oxide (Formula I) andlithium/nickel/cobalt/manganese composite oxide (Formula II) ispreferably in the range of 90:10 to 10:90 (w/w). If the content of thecomposite oxide (I) among two composite oxides is excessively low, thestability of the battery is lowered. Conversely, if the content of thecomposite oxide (II) is excessively low, it is undesirably difficult toachieve desired life characteristics. These facts will also beillustrated and confirmed in the following Examples and ComparativeExamples hereinafter.

Methods of preparing lithium metal composite oxides such aslithium/manganese spinel oxides of Formula I andlithium/nickel/cobalt/manganese composite oxides of Formula II arewell-known in the art and thus will not be described herein.

Hereinafter, fabrication of a cathode containing a cathode activematerial according to the present invention will be specificallyillustrated.

First, the cathode active material of the present invention, and abinder and a conductive material in a content of 1 to 20% by weightrelative to the active material are added to a dispersion solvent andthe resulting dispersion is stirred to prepare an electrode paste. Thepaste is applied to a metal plate for a current collector which is thencompressed and dried to fabricate a laminate electrode.

The cathode current collector is generally fabricated to have athickness of 3 to 500 μm. There is no particular limit to the cathodecurrent collector, so long as it has high conductivity without causingchemical changes in the fabricated battery. As examples of the cathodecurrent collector, mention may be made of stainless steel, aluminum,nickel, titanium, sintered carbon, and aluminum or stainless steel whichwas surface-treated with carbon, nickel, titanium or silver. The currentcollector may be fabricated to have fine irregularities on the surfacethereof so as to enhance adhesion to the cathode active material. Inaddition, the current collector may take various forms including films,sheets, foils, nets, porous structures, foams and non-woven fabrics.

As examples of the binder that may be utilized in the present invention,mention may be made of polytetrafluoroethylene (PTFE), polyvinylidenefluoride (PVdF), cellulose, polyvinyl alcohols, carboxymethylcellulose(CMC), starch, hydroxypropylcellulose, regenerated cellulose, polyvinylpyrrolidone, tetrafluoroethylene, polyethylene, polypropylene,ethylene-propylene-diene terpolymer (EPDM), sulfonated EPDM, styrenebutadiene rubber, fluoro rubber and various copolymers.

There is no particular limit to the conductive material, so long as ithas suitable conductivity without causing chemical changes in thefabricated battery. As examples of conductive materials, mention may bemade of conductive materials, including graphite such as natural orartificial graphite; carbon blacks such as carbon black, acetyleneblack, Ketjen black, channel black, furnace black, lamp black andthermal black; conductive fibers such as carbon fibers and metallicfibers; metallic powders such as carbon fluoride powder, aluminum powderand nickel powder; conductive whiskers such as zinc oxide and potassiumtitanate; conductive metal oxides such as titanium oxide; andpolyphenylene derivatives. Specific examples of commercially availableconductive materials may include various acetylene black products(available from Chevron Chemical Company, Denka Singapore PrivateLimited and Gulf Oil Company), Ketjen Black EC series (available fromArmak Company), Vulcan XC-72 (available from Cabot Company) and Super P(Timcal Co.).

Where appropriate, the filler may be optionally added as an ingredientto inhibit cathode expansion. There is no particular limit to thefiller, so long as it does not cause chemical changes in the fabricatedbattery and is a fibrous material. As examples of the filler, there maybe used olefin polymers such as polyethylene and polypropylene; andfibrous materials such as glass fiber and carbon fiber.

Representative examples of the dispersion solvent that can be used inthe present invention may include isopropyl alcohol, N-methylpyrrolidone (NMP) and acetone.

Uniform application of the paste of electrode materials to a metalmaterial may be carried out by conventional methods known in the art orappropriate novel methods, taking into consideration characteristics ofmaterials to be used. For example, preferably the electrode paste isdistributed onto the current collector and is then uniformly dispersedthereon using a doctor blade. Where appropriate, distribution anddispersion of the electrode paste may also be performed in a singlestep. Further, application of the electrode paste may be carried out bya method selected from die casting, comma coating, screen printing andthe like. Alternatively, application of the electrode paste may becarried out by molding the paste on a separate substrate and thenbinding it to the current collector via pressing or lamination.

Drying of the paste applied over the metal plate is preferably carriedout in a vacuum oven at 50 to 200° C. for 1 to 3 days.

Further, the present invention provides a lithium secondary batterycomprising an electrode assembly composed of the above-fabricatedcathode and an anode, which are arranged opposite to each other with aseparator therebetween, and a lithium salt-containing, non-aqueouselectrolyte.

The anode is, for example, fabricated by applying an anode activematerial to an anode current collector, followed by drying. If desired,the anode may further optionally include other components such asconductive material, binder and filler, as described above.

The anode current collector is generally fabricated to have a thicknessof 3 to 500 μm. There is no particular limit to the anode currentcollector, so long as it has suitable conductivity without causingchemical changes in the fabricated battery. As examples of the anodecurrent collector, mention may be made of copper, stainless steel,aluminum, nickel, titanium, sintered carbon, copper or stainless steelhaving a surface treated with carbon, nickel, titanium or silver, andaluminum-cadmium alloys. Similar to the cathode current collector, theanode current collector may also be fabricated to form fineirregularities on the surface thereof so as to enhance adhesion to theanode active material. In addition, the anode current collector may takevarious forms including films, sheets, foils, nets, porous structures,foams and non-woven fabrics.

As examples of the anode materials utilizable in the present invention,mention may be made of carbon such as non-graphitizing carbon andgraphite based carbon; metal composite oxides such as Li_(x)Fe₂O₃(0≦x≦1), Li_(x)WO₂ (0≦x≦1) and Sn_(x)Me_(1−x)Me′_(y)O_(z) (Me: Mn, Fe,Pb, Ge; Me′: Al, B, P, Si, Group I, Group II and Group III elements ofthe Periodic Table of the Elements, halogen atoms; 0<x≦1; 1≦y≦3; and1≦z≦8); lithium metals; lithium alloys; silicon based alloys; tin basedalloys; metal oxides such as SnO, SnO₂, PbO, PbO₂, Pb₂O₃, Pb₃O₄, Sb₂O₃,Sb₂O₄,Sb₂ O₅, GeO, GeO₂, Bi₂O₃, Bi₂O₄, and Bi₂O₅; conductive polymerssuch as polyacetylene; and Li-Co-Ni based materials.

The separator is interposed between the cathode and anode. As theseparator, an insulating thin film having high ion permeability andmechanical strength is used. The separator typically has a pore diameterof 0.01 to 10 μm and a thickness of 5 to 300 μm. As the separator,sheets or non-woven fabrics, or kraft papers made of an olefin polymersuch as polypropylene and/or glass fibers or polyethylene, which havechemical resistance and hydrophobicity, are used. Typical examples ofcommercially available products for the separator may include Celgardseries such as Celgard™2400 and 2300 (available from Hoechst CelaneseCorp.), polypropylene separators (available from Ube Industries Ltd., orPall RAI Co.) and polyethylene series (available from Tonen or Entek).

Where appropriate, a gel polymer electrolyte may be coated on theseparator to increase the battery stability. Representative examples ofthe gel polymer may include polyethylene oxide, polyvinylidene fluorideand polyacrylonitrile.

When a solid electrolyte such as a polymer is employed as theelectrolyte, the solid electrolyte may also serve as both the separatorand electrolyte.

The lithium salt-containing non-aqueous electrolyte is composed of anon-aqueous electrolyte and lithium. As the non-aqueous electrolyte, anon-aqueous electrolytic solution, organic solid electrolyte andinorganic solid electrolyte may be utilized.

As examples of the non-aqueous electrolytic solution that can be used inthe present invention, mention may be made of non-protic organicsolvents such as N-methyl-2-pyrollidinone, propylene carbonate, ethylenecarbonate, butylene carbonate, dimethyl carbonate, diethyl carbonate,ethylmethyl carbonate, gamma-butyrolactone, 1,2-dimethoxy ethane,1,2-diethoxy ethane, tetrahydroxy Franc, 2-methyl tetrahydrofuran,dimethylsulfoxide, 1,3-dioxolane, 4-methyl-1,3-dioxene, diethylether,formamide, dimethylformamide, dioxolane, acetonitrile, nitromethane,methyl formate, methyl acetate, phosphoric acid triester, trimethoxymethane, dioxolane derivatives, sulfolane, methyl sulfolane,1,3-dimethyl-2-imidazolidinone, propylene carbonate derivatives,tetrahydrofuran derivatives, ether, methyl propionate and ethylpropionate.

As examples of the organic solid electrolyte utilized in the presentinvention, mention may be made of polyethylene derivatives, polyethyleneoxide derivatives, polypropylene oxide derivatives, phosphoric acidester polymers, poly agitation lysine, polyester sulfide, polyvinylalcohol, polyvinylidene fluoride, and polymers containing ionicdissociation groups.

As examples of the inorganic solid electrolyte utilized in the presentinvention, mention may be made of nitrides, halides and sulphates oflithium such as Li₃N, LiI, Li₅NI₂, Li₃N—LiI—LiOH, LiSiO₄,LiSiO₄—LiI—LiOH, Li₂SiS₃, Li₄SiO₄, Li ₄SiO₄—LiI—LiOH andLi₃PO₄—Li₂S—SiS₂.

The lithium salt is a material that is readily soluble in theabove-mentioned non-aqueous electrolyte and may include, for example,LiCl, LiBr, LiI, LiClO₄, LiBF₄, LiB₁₀Cl₁₀, LiPF₆, LiCF₃SO₃, LiCF₃CO₂,LiAsF₆, LiSbF₆, LiAlCl₄, CH₃SO₃Li, CF₃SO₃Li, LiSCN, LiC(CF₃SO₂)₃,(CF₃SO₂)₂NLi, chloroborane lithium, lower aliphatic carboxylic acidlithium, lithium tetraphenyl borate and imide.

Additionally, in order to improve charge/discharge characteristics andflame retardancy, for example, pyridine, triethylphosphite,triethanolamine, cyclic ether, ethylenediamine, n-glyme, hexaphosphorictriamide, nitrobenzene derivatives, sulfur, quinone imine dyes,N-substituted oxazolidinone, N,N-substituted imidazolidine, ethyleneglycol dialkyl ether, ammonium salts, pyrrole, 2-methoxy ethanol,aluminum trichloride or the like may be added to the non-aqueouselectrolyte. If necessary, in order to impart incombustibility, thenon-aqueous electrolyte may further include halogen-containing solventssuch as carbon tetrachloride and ethylene trifluoride. Further, in orderto improve high-temperature storage characteristics, the non-aqueouselectrolyte may additionally include carbon dioxide gas.

EXAMPLES

Now, the present invention will be described in more detail withreference to the following Examples. These examples are provided onlyfor illustrating the present invention and should not be construed aslimiting the scope and spirit of the present invention.

Example 1

A substituted lithium/manganese spinel oxide ofLi_(1+x)Mn_(1.95)Al_(00.5)O₄ and a lithium/nickel/cobalt/manganesecomposite oxide of Li_(1+z)Ni_(1/3)Co_(1/3)Mn_(1/3)O₂ were mixed in aweight ratio of 1:1 to thereby prepare a cathode active material. Thecathode active material was mixed with 5% by weight of carbon black and5% by weight of PVdF as a binder, and stirred with NMP as a solvent. Theresulting mixture was coated on aluminum foil as a metal currentcollector which was then dried in a vacuum oven at 120° C. for more than2 hours, thereby fabricating a cathode.

An electrode assembly was fabricated using the thus-fabricated cathode,an anode which was fabricated by coating mesocarbon microbeads (MCMBs)as artificial graphite on copper foil, and a porous separator made ofpolypropylene. The electrode assembly was placed in a pouch case towhich electrode leads were then connected. Thereafter, as anelectrolyte, a solution of ethylene carbonate (EC) and dimethylcarbonate (DMC) (1:1, v/v), in which 1M LiPF₆ salt was dissolved, wasinjected thereto, followed by sealing the case to assemble a lithiumsecondary battery.

The thus-fabricated lithium secondary battery was subjected tocharge/discharge cycling in a voltage range of 3.0 to 4.2 V and lifecharacteristics of the battery were measured. The results thus obtainedare given in Table 1 below.

Example 2

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide ofLi_(1+x)Mn_(1.9)Al_(0.1)O₄, instead of usingLi_(1+x)Mn_(1.95)Al_(0.05)O₄. The thus-fabricated lithium secondarybattery was subjected to charge/discharge cycling in a voltage range of3.0 to 4.2 V and life characteristics of the battery were measured. Theresults are given in Table 1 below.

Example 3

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide ofLi_(1+x)Mn_(1.8)Al_(0.2)O₄, instead of usingLi_(1+x)Mn_(1.95)Al_(0.05)O₄. The thus-fabricated lithium secondarybattery was subjected to charge/discharge cycling in a voltage range of3.0 to 4.2 V and life characteristics of the battery were measured. Theresults are given in Table 1 below.

Example 4

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide ofLi_(1+x)Mn_(1.95)Mg_(0.05)O₄, instead of usingLi_(1+x)Mn_(1.95)Al_(0.05)O₄. The thus-fabricated lithium secondarybattery was subjected to charge/discharge cycling in a voltage range of3.0 to 4.2 V and life characteristics of the battery were measured. Theresults are given in Table 1 below.

Example 5

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide ofLi_(1+x)Mn_(1.9)Mg_(0.1)O₄, instead of usingLi_(1+x)Mn_(1.95)Al_(0.05)O₄. The thus-fabricated lithium secondarybattery was subjected to charge/discharge cycling in a voltage range of3.0 to 4.2 V and life characteristics of the battery were measured. Theresults are given in Table 1 below.

Example 6

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide ofLi_(1+x)Mn_(1.8)Mg_(0.2)O₄, instead of usingLi_(1+x)Mn_(1.95)Al_(0.05)O₄. The thus-fabricated lithium secondarybattery was subjected to charge/discharge cycling in a voltage range of3.0 to 4.2 V and life characteristics of the battery were measured. Theresults are given in Table 1 below.

Comparative Example 1

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using anon-substituted lithium/manganese spinel oxide of Li_(1+x)Mn₂O₄, insteadof using Li_(1+x)Mn_(1.95)Al_(0.05)O₄. The thus-fabricated lithiumsecondary battery was subjected to charge/discharge cycling in a voltagerange of 3.0 to 4.2 V and life characteristics of the battery weremeasured. The results are given in Table 1 below.

TABLE 1 Subsititution Life characteristics Substituent amount of(Capacity at 300 cycles metal ions metal ions (y) relative to initialcapacity, %) Example 1 Al 0.05 78 Example 2 Al 0.1 84 Example 3 Al 0.285 Example 4 Mg 0.05 80 Example 5 Mg 0.1 82 Example 6 Mg 0.2 83 Comp. —0 56 Example 1

As can be seen from Table 1, in the composite oxide mixtures of thecathode active materials, substitution of a manganese (Mn) site of thelithium/manganese spinel oxide with aluminum (Al) or magnesium (Mg) hasled to significant improvements in life characteristics of the battery.In addition, the higher substitution amounts (y-value) of metal ionshave led to further improvements in life characteristics. However, aswill be seen in Comparative Examples 2 and 3 hereinafter, it wasconfirmed that when the substitution amount, i.e., the y value, exceeds0.2, the initial capacity of the battery is decreased.

Comparative Example 2

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide ofLi_(1+x)Mn_(1.7)Al_(0.3)O₄. The thus-fabricated lithium secondarybattery was subjected to charge/discharge cycling in a voltage range of3.0 to 4.2 V, and the initial capacity of the battery was measured andcompared with the secondary battery of Example 1. The results haveconfirmed 14% decrease of battery capacity, relative to the initialcapacity of the secondary battery of Example 1.

Comparative Example 3

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using alithium/manganese spinel oxide of Li_(1+x)Mn_(1.7)Mg_(0.3)O₄. Thethus-fabricated lithium secondary battery was subjected tocharge/discharge cycling in a voltage range of 3.0 to 4.2 V, and theinitial capacity of the battery was measured and compared with thesecondary battery of Example 1. The results have confirmed 24% decreaseof battery capacity, relative to the initial capacity of the secondarybattery of Example 1.

Example 7

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide of Li_(1+x)Mn_(1.9)Al_(0.1)O₄and a lithium/nickel/cobalt/manganese composite oxide ofLi_(1+z)Ni_(1/3)Co_(1/3)Mn_(1/3)O₂ in a weight ratio of 90:10. Thethus-fabricated lithium secondary battery was subjected tocharge/discharge cycling in a voltage range of 3.0 to 4.2 V and lifecharacteristics of the battery were measured. The results are given inTable 2 below.

Example 8

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide of Li_(1+x)Mn_(1.9)Al_(0.1)O₄and a lithium/nickel/cobalt/manganese composite oxide ofLi_(1+z)Ni_(1/3)Co_(1/3)Mn_(1/3)O₂ in a weight ratio of 70:30. Thethus-fabricated lithium secondary battery was subjected tocharge/discharge cycling in a voltage range of 3.0 to 4.2 V and lifecharacteristics of the battery were measured. The results are given inTable 2 below.

Example 9

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide of Li_(1+x)Mn_(1.9)Al_(0.1)O₄and a lithium/nickel/cobalt/manganese composite oxide ofLi_(1+z)Ni_(1/3)Co_(1/3)Mn_(1/3)O₂ in a weight ratio of 50:50 (1:1). Thethus-fabricated lithium secondary battery was subjected tocharge/discharge cycling in a voltage range of 3.0 to 4.2 V and lifecharacteristics of the battery were measured. The results are given inTable 2 below.

Example 10

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide of Li_(1+x)Mn_(1.9)Al_(0.1)O₄and a lithium/nickel/cobalt/manganese composite oxide ofLi_(1+z)Ni_(1/3)Co_(1/3)Mn_(1/3)O₂ in a weight ratio of 30:70. Thethus-fabricated lithium secondary battery was subjected tocharge/discharge cycling in a voltage range of 3.0 to 4.2 V and lifecharacteristics of the battery were measured. The results are given inTable 2 below.

Example 11

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide of Li_(1+x)Mn_(1.9)Al_(0.1)O₄and a lithium/nickel/cobalt/manganese composite oxide ofLi_(1+z)Ni_(1/3)Co_(1/3)Mn_(1/3)O₂ in a weight ratio of 10:90. Thethus-fabricated lithium secondary battery was subjected tocharge/discharge cycling in a voltage range of 3.0 to 4.2 V and lifecharacteristics of the battery were measured. The results are given inTable 2 below.

Comparative Example 4

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using onlya substituted lithium/manganese spinel oxide ofLi_(1+x)Mn_(1.9)Al_(0.1)O₄. The thus-fabricated lithium secondarybattery was subjected to charge/discharge cycling in a voltage range of3.0 to 4.2 V and life characteristics of the battery were measured. Theresults are given in Table 2 below.

Comparative Example 5

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using onlya lithium/nickel/cobalt/manganese composite oxide ofLi_(1+z)Ni_(1/3)Co_(1/3)Mn_(1/3)O₂. The thus-fabricated lithiumsecondary battery was subjected to charge/discharge cycling in a voltagerange of 3.0 to 4.2 V and life characteristics of the battery weremeasured. The results are given in Table 2 below.

TABLE 2 Weight ratio Weight ratio Life of 10% of lithium/characteristics Al-substituted nickel/cobalt/ (Capacity at 300lithium/manga- manganese cycles relative to nese spinel composite oxideintial capacity, %) Example 7 90 10 81 Example 8 70 30 82 Example 9 5050 84 Example 10 30 70 82 Example 11 10 90 81 Comp. 100 0 64 Example 4Comp. 0 100 80 Example 5

As can be seen from Table 2, life characteristics of the battery beganto improve when more than 10% lithium/nickel/cobalt/manganese compositeoxide was added to the Al-substituted lithium/manganese spinel oxide,and it could be confirmed that the thus-obtained life characteristicsare similar to life characteristics achieved upon addition of more than30% lithium/nickel/cobalt/manganese composite oxide. However, anexcessively high content of the lithium/nickel/cobalt/manganesecomposite oxide may result in relatively low safety of the battery andtherefore it is preferred to use the lithium/nickel/cobalt/manganesecomposite oxide in an amount of less than 90%.

Example 12

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide of Li_(1+x)Mn_(1.9)Al_(0.1)O₄and a lithium/nickel/cobalt/manganese composite oxide ofLi_(1+z)Ni_(0.4)Mn_(0.4)Co_(0.2)O₂ in a weight ratio of 90:10. Thethus-fabricated lithium secondary battery was subjected tocharge/discharge cycling in a voltage range of 3.0 to 4.2 V and lifecharacteristics of the battery were measured. The results are given inTable 3 below.

Example 13

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide of Li_(1+x)Mn_(1.9)Al_(0.1)O₄and a lithium/nickel/cobalt/manganese composite oxide ofLi_(1+z)Ni_(0.4)Mn_(0.4)Co_(0.2)O₂ in a weight ratio of 70:30. Thethus-fabricated lithium secondary battery was subjected tocharge/discharge cycling in a voltage range of 3.0 to 4.2 V and lifecharacteristics of the battery were measured. The results are given inTable 3 below.

Example 14

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide of Li_(1+x)Mn_(1.9)Al_(0.1)O₄and a lithium/nickel/cobalt/manganese composite oxide ofLi_(1+z)Ni_(0.4)Mn_(0.4)Co_(0.2.)O₂ in a weight ratio of 50:50 (1:1).The thus-fabricated lithium secondary battery was subjected tocharge/discharge cycling in a voltage range of 3.0 to 4.2 V and lifecharacteristics of the battery were measured. The results are given inTable 3 below.

Example 15

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide of Li_(1+x)Mn_(1.9)Al_(0.1)O₄and a lithium/nickel/cobalt/manganese composite oxide ofLi_(1+z)Ni_(0.4)Mn_(0.4)Co_(0.2)O₂ in a weight ratio of 30:70. Thethus-fabricated lithium secondary battery was subjected tocharge/discharge cycling in a voltage range of 3.0 to 4.2 V and lifecharacteristics of the battery were measured. The results are given inTable 3 below.

Example 16

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using asubstituted lithium/manganese spinel oxide of Li_(1+x)Mn_(1.9)Al_(0.1)O₄and a lithium/nickel/cobalt/manganese composite oxide ofLi_(1+z)Ni_(0.4)Mn_(0.4)Co_(0.2)O₂ in a weight ratio of 10:90. Thethus-fabricated lithium secondary battery was subjected tocharge/discharge cycling in a voltage range of 3.0 to 4.2 V and lifecharacteristics of the battery were measured. The results are given inTable 3 below.

Comparative Example 6

A lithium secondary battery was assembled in the same manner as inExample 1, except that a cathode active material was prepared using onlya lithium/nickel/cobalt/manganese composite oxide ofLi_(1+z)Ni_(0.4)Mn_(0.4)Co_(0.2)O₂. The thus-fabricated lithiumsecondary battery was subjected to charge/discharge cycling in a voltagerange of 3.0 to 4.2 V and life characteristics of the battery weremeasured. The results are given in Table 3 below.

TABLE 3 Weight ratio Weight ratio Life of 10% of lithium/characteristics Al-substituted nickel/cobalt/ (Capacity at 300lithium/manga- manganese cycles relative to nese spinel composite oxideintial capacity, %) Example 12 90 10 81 Example 13 70 30 81 Example 1450 50 84 Example 15 30 70 82 Example 16 10 90 80 Comp. 100 0 64 Example4 Comp. 0 100 78 Example 6

As can be seen from Table 3, life characteristics of the battery beganto improve when more than 10% lithium/nickel/cobalt/manganese compositeoxide was added to the Al-substituted lithium/manganese spinel, and itcould be confirmed that the thus-obtained life characteristics aresimilar to life characteristics achieved upon addition of more than 30%lithium/nickel/cobalt/manganese composite oxide. However, an excessivelyhigh content of the lithium/nickel/cobalt/manganese composite oxide mayresult in relatively low safety of the battery and therefore it ispreferred to use the lithium/nickel/cobalt/manganese composite oxide inan amount of less than 90%.

INDUSTRIAL APPLICABILITY

As apparent from the above description, a lithium secondary batteryusing a mixture of a manganese spinel oxide having a substitution of amanganese (Mn) site with a certain metal element and a certainlithium/nickel/cobalt/manganese composite oxide, according to thepresent invention, as a cathode active material, can secure safety ofthe battery and improve a service life thereof, even under high current,short period charge/discharge cycle conditions.

Although the preferred embodiments of the present invention have beendisclosed for illustrative purposes, those skilled in the art willappreciate that various modifications, additions and substitutions arepossible, without departing from the scope and spirit of the inventionas disclosed in the accompanying claims.

1. A cathode active material for a lithium secondary battery, comprisinga mixture of a lithium/manganese cathode oxide represented by Formula Iand a lithium/nickel/cobalt/manganese oxide represented by Formula II:Li_(1+x)Mn_(2−y)M_(y)O₄  (I)Li_(1+z)Ni_(0.4)Mn_(0.4)CO_(0.2)O₂  (II) wherein, M is a metal having anoxidation number of 2 to 3; 0≦x≦0.2; 0<y≦0.2; 0≦z≦0.1; Wherein, themixture of the lithium/manganese spinel oxide of Formula I and thelithium/nickel/cobalt/manganese composite oxide of Formula II is in theratio of 30:70 to 70:30 by weight.
 2. The cathode active materialaccording to claim 1, wherein M in Formula I is aluminum (Al), magnesium(Mg) or both of them.
 3. The cathode active material according to claim1, wherein the value of y is in the range of 0.01 to 0.2.
 4. A lithiumsecondary battery comprising the cathode active material of claim
 1. 5.A lithium secondary battery comprising the cathode active material ofclaim
 2. 6. A lithium secondary battery comprising the cathode activematerial of claim
 3. 7. A lithium secondary battery comprising thecathode active material of claim 1.